Mgf2 Crystal Magnesium Fluoride
Descriptions: MgF2 or Magnesium Fluoride is positive uni-axial crystal with a very high optical transmittance from the v
Send your inquiryDESCRIPTION
Basic Info
Model NO. | Dia1-20*0.1-220 |
Specification | customized |
Trademark | optu |
Origin | Chengdu |
HS Code | 9001909090 |
Production Capacity | 5000 Pieces / Year |
Product Description
Descriptions:
MgF2 or Magnesium Fluoride is positive uni-axial crystal with a very high optical transmittance from the vacuum UV to IR. It is regularly used for optical elements where extreme ruggedness and durability is required.
Main application:
1) VUV , UV ,IR optical systems
2) UV photomultiplier tubes
3) Excimer lasers
4) Optical fiber communications industry
Advantages:
1) High optical transmittance from the vacuum ultraviolet to the infrared spectrum region(0.12~8.5μm).
2) Resistance to mechanical , thermal shock and radiation
3) Chemically stable
4) A positive birefringent crystal
5) Used for Optical prisms, lenses, wedges, windows, other optical components etc
Basic properties of MgF2 crystal:
Chemical Formula | MgF2 |
Density | 3.18 g/cm3 |
Melting Point | 1255ºC |
Boiling Point | 2239ºC |
Molar Mass | 62.32 |
Thermal Conductivity | 3.15W/m K |
Specific Heat | 920 J/(kg K) |
Thermal Expansion Coefficient | ⊥C 9×10-6∥C 14 ×10-6 / K |
Knoop Hardness | 415,576 kg/mm2 |
Mohs Hardness | 5--6 |
Young's Modulus | 138.5 GPa |
Shear Modulus | 54.66 GPa |
Bulk Modulus | 101.32 GPa |
Rupture Modulus | 49.6 MPa |
Elastic Coefficient | C11=140 C12=89 C44=57 C13=63 C66=96 |
Dielectric Constant | 105 ~107 Hz 5.45 |
Solubility in Water | 0.0076 g / 100 g, 18ºC |
Lattice Parameter | a=4.64 Å, c=3.06 Å |
Crystal Type | Tetragonal, P42/mnm |
Cleavage Planes | (100), (110) |
Absorption Coefficient | 0.07 at 0.2µm,0.02 at 5.0µm |
Poisson's Ratio | 0.276 |
Transmission Range | 0.11 - 8.5 |
Vapor Pressure | 1 Pa(at 1150ºC), 10 Pa(at 1300ºC) |
Applications | IR, UV , DUV and VUV |
Fluorescence | Weak yellow upon excitation at 590 nm |
OPTU offers MgF2 specifications:
Orientation: | a-cut or <100> ;C-cut or<001>; random (-RM) or as specified |
Wavefront Distortion: | λ/6 per inch @ 632.8 nm |
Dimension Tolerances: | rods with diameter: +0.0/-0.05 mm , Length: ±0.1 mm |
Surface Quality: | 20/10 Scratch/Dig MIL-O-1380A |
Parallelism: | < 20″ |
Perpendicularity: | < 10′ |
Clear Aperture: | > 85% |
Surface Flatness: | < λ/6 @ 632.8 nm |
Chamfer: | < 0.25 mm @ 45deg. |
Size | Upon customer request |
Coating | Uncoated or upon customer's request |
Quality Warranty Period | One year under proper use |
Related Products
-
Polished Litao3 Nonlinear Crystal for Applications in Acoustic, Electro-Optical Devices
-
Supply Single Crystal Silicon Wafer Si Substrate Type N/P for Infrared Optical Materials
-
Empty Glass Vial 15ml, Different Color Scintillation Vial with Cap
-
Aspheric Lens Laser Module Collimating Lens Focusing Projector Optical Glass Customization